C95500 Material Data Sheet

Element

Nominal %

Minimum %

Maximum %

Aluminum

11

10

11.5

Antimony

-

-

-

Copper

81

78

-

Iron

4

3

5

Lead

-

-

-

Nickel

4

3

5.5

Phosphorus

-

-

-

Silicon

-

-

-

Sulfur

-

-

-

Tin

-

-

-

Zinc

-

-

3.5

MO1 - As Sand Cast

Tensile Strength:

Minimum 90 ksi

Yield Strength:

Minimum 40 ksi - 0.5% Ext. under load

Elongation:

Minimum 6% in 2 in.

Brinell Hardness:

190 @ 3000 kg load

M02 - As Centrifugal Cast

Tensile Strength:

Minimum 90 ksi

Yield Strength:

Minimum 40 ksi - 0.5% Ext. under load

Elongation:

Minimum 6%, in 2 inches

Brinell Hardness:

190 @ 3000 kg load

M07 - As Continuous Cast

Tensile Strength:

Minimum 95 ksi

Yield Strength:

Minimum 42 ksi - 0.5% Ext. under load

Elongation:

10%, in 2 inches

Property

US Customary

Melting Point - Liquidus

1930 F

Melting Point - Solidus

1900 F

Density

0.272 lb/cu in @ 68 F

Specific Gravity

7.53

Specific Heat Capacity

0.1 Btu/lb/oF at 68 F

Coefficient of Thermal Expansion

9.0 ·10-6 per oF (68-572 F)

Thermal Conductivity

24.2 Btu · ft/(hr · ft2·oF)at 68F

Electrical Conductivity

8% IACS @ 68 F

Electrical Resistivity

122.8 ohms-cmil/ft @ 68 F

Modulas of Elasticity in Tension

16,000 ksi

Joining Methods

Suitability

Soldering

Not Recommended

Brazing

Fair

Oxyacetylene Welding

Not Recommended

Gas Shielded Arc Welding

Good

Coated Metal Arc Welding

Good

Machinability (C360 Brass =100)

50